求教H13材料元素分析

likeooo

以下4块不同厂家H13材料取样的抽查,光谱分析结果.
C
Si
S
P
Mn
Cr
Mo
V
Fe
0.229
0.827
0.0058
0.001
0.333
5.354
0.603
1.023
91.035%



C

Si
S
P
Mn
Cr
Mo
V
Fe
0.216
0.687
0.0059
0.001
0.312
5.394

0.560
0.993

91.21%
     
C
Si
S
P
Mn
Cr
Mo
V
Fe
0.215
0.901
0.0058
0.001
0.386

5.27
0.549
0.92

91.07%
     
C
Si
S
P
Mn
Cr
Mo
V
Fe
0.2546
0.878
0.0059
0.006
0.298
5.703
0.634
1.007
90.5004%


顺便问下:通用FE通道做出来的数值会有所偏差吗?会偏差很多吗?

likeooo

C                Si            S            P             Mn        Cr           Mo        V             Fe
0.229     0.827    0.0058    0.001     0.333    5.354    0.603   1.023   91.035%
   
C               Si             S             P           Mn          Cr        Mo         V          Fe
0.216    0.687    0.0059    0.001     0.312    5.394    0.560   0.993   91.21%

C            Si                 S             P          Mn       Cr         Mo         V         Fe
0.215    0.901    0.0058    0.001    0.386     5.27    0.549   0.92    91.07%

C              Si            S            P            Mn         Cr          Mo          V            Fe
0.2546    0.878    0.0059   0.006    0.298    5.703    0.634   1.007   90.5004%

小五子

中国的4Cr5MoSiV1（近似美国的H13）标准化学成分:
        C                                Si                            S   、 P              Mn                                  Cr                            Mo
0.32-0.45                  0.80-1.20                       ≤0.030             0.20-0.50                   4.75-5.50         1.10-1.75
       V
0.80-1.20

-

小五子

C（0.32-0.45），Si（0.80-1.20），S、P（≤0.030）， Mn （ 0.20-0.50  ）    ， Cr（  4.75-5.50         ）， Mo（   1.10-1.75）， V（0.80-1.20 ）

likeooo

C和钼元素的不够,有什么方面的影响

sadzhli

老兄你用的什么光谱分析仪?

maxdew

C含量和硬度有关。

戴铭

没看明白，是一个样分析的4个结果？还是......
仪器分析的准确与否用标样验证，或化学法验证。
如果分析再现性不好，可分析样品表面是否有缺陷、污染，电极污染与高度，真空度，激发电源的稳定等因素。

choylove

MO元素和存在不锈钢中能极大提高防腐蚀性能
也能和C形成碳化物 而且硬度是大于碳化洛的
在热作钢当中的作用是提高钢红硬性和抗热疲劳能力

likeooo

谢谢，上面是4块材料的分析报告.
楼上的兄弟,你说MO元素的问题还是看不明白
我们现在客户反映的断裂和腐蚀现象确实存在