有检测螺栓的吗？进来看看国标是不是出现一个低级的错误？？

烟台

烟台

国标GB/T3098.1-2000 中第14 15页有关脱碳试验的规定   上述图中划红线部分是不是错了

图示下部是HV3≤HV2+30   而后面的文字描述又变成第一点了

烟台

到底是 1点  还是2 点

MYG

没接触过这个标准，建议去问标准制订者。

皮猴

iso898-5 1998 中也是一样的，看来国标就抄抄没想过错
我看有2007年的更新版出来了，楼主可以去查查

附98版
HV2 > HV1 –30
HV3 < HV2 +30
Key
1, 2, 3 Measurement points
4 Pitch line
Figure 2 — Hardness measurements for decarburization test


Hardness determination for point 3 shall be made on the pitch line of the thread adjacent to the thread on which
determinations at points 1 and 2 are made.
The Vickers hardness value at point 2 (HV2) shall be equal to or greater than that at point 1 (HV1) minus 30 Vickers units. In
this case the height of the non-decarburized zone E is at least as specified in table 4.
The Vickers hardness value at point 3 (HV3) shall be equal to or less than that at point 1 (HV1) plus 30 Vickers units. An
increase of more than 30 Vickers units indicates that carburization is not permissible.
Complete decarburization up to the maximum specified in table 3 cannot be detected by the hardness measurement
method.
NOTE — Careful differentiation should be made between an increase in hardness caused by carburization and that due to heat treatment
or cold working of the surface.

皮猴

我觉得是第一点，是用来检验增碳的话用以1为标准好一点
第2点是用来衡量脱碳深度的

第3点比第二点高30度，不能说明增碳，也可能是未脱碳，不可能出现这种纰漏
所以我觉得是第一点

烟台

皮猴 发表于 2012-2-3 15:51
iso898-5 1998 中也是一样的，看来国标就抄抄没想过错
我看有2007年的更新版出来了，楼主可以去查查

灰常谢谢 ..........

烟台

皮猴 发表于 2012-2-3 15:58
我觉得是第一点，是用来检验增碳的话用以1为标准好一点
第2点是用来衡量脱碳深度的

2010版 是第一点   ........