王申存 1 ，李志成 1 ，易丹青 1 ，曹志强 2 ，张鸿 1
(1. 中南大学 材料科学与工程学院，湖南 长沙，410083；
2. 湖南华菱湘潭钢铁有限公司，湖南 湘潭，411101)
摘要：为了研究马氏体的相变特征，利用电子背散射衍射(EBSD)技术并结合金相显微镜和显微硬度计分析低温回火的 20MnCr5 渗碳齿轮钢的性能和组织。根据马氏体相变理论中的 KS 和 NW取向关系分别计算得到马氏体{110}α 极射赤面投影图。利用 EBSD 技术对 20MnCr5 齿轮钢心部选定的区域进行扫描，分析区域中马氏体的取向分布特征。研究结果表明：马氏体取向整体呈随机分布，但在局部区域呈有规律分布。整个扫描区域的取向差主要分布在 5°以下和 45°以上。为反映马氏体局部区域取向分布的规律，选定一个原奥氏体晶粒，并做出区域中所有马氏体{110}α 晶面的极射赤面投影图，得到极点有规律分布的极图。通过对{110}α 极图分别使用KS和NW
关系拟合，确定所选区域的马氏体的取向关系以 NW 关系为主，实际极点离散分布在理论极点周围；使用协同形变机理解释实际取向分布与理论分布的偏差是由马氏体相变导致周围组织复杂的畸变引起。
关键词：20MnCr5；电子背散射衍射技术；马氏体变体；取向关系
中图分类号：TG111.5 文献标志码：A 文章编号：1672−7207(2011)09−2620−08

Orientation relationship of low temperature tempered Martensite
investigated by electron back scattered diffraction
WANG Shencun
1 , LI Zhicheng
1 , YI Danqing
1 , CAO Zhiqiang
2 , ZHANG Hong 1
(1. School of Materials Science and Engineering, Central South University, Changsha 410083, China;
2. Hunan Valin Xiangtan Iron and Steel Co. Ltd., Xiangtan 411101, China)
Abstract: Microhardness tester, optical microscope and electron back scattered diffraction technique were used to
examine the property and microstructure of a low temperature tempered 20MnCr5 carburized gear. {110}α polar figure of
Martensite was calculated according to the KS and NW orientation relationship. Orientation distribution of Martensite
at the center of the gear was examined by electron back scattered diffraction technique. {110}α polar figure of Martensite in a selected prior austenite grain was plotted. The orientation distributes randomly in the whole scanned area, but distributes regularly in local area. The misorientation of the scanned area distributes mainly below 5° and above 45°. In order to characterize the orientation distribution law in local areas, stereographic projection of Martensite {110}α in a selected prior austenite area was plotted. The orientation relationship in the selected prior austenite is determined to be mainly NW orientation by fitting the polar figure. Discrepancy between practical and theoretical orientation distribution is interpreted by cooperative strain mechanism.
Key words: 20MnCr5; electron back scattered diffraction; Martensite variants; orientation relationship